Title: Fibre microstructure and mechanics of atherosclerotic plaques
Author: Douglas, Graeham Rees
ISNI:       0000 0004 7226 4662
Awarding Body: University of Cambridge
Current Institution: University of Cambridge
Date of Award: 2018
Availability of Full Text:
Access from EThOS:
Full text unavailable from EThOS. Please try the link below.
Access from Institution:
Atherosclerosis is characterised by the progressive growth of a plaque, where a fibrous cap covers a lipid-rich core. Rupture of this fibrous cap can lead to thrombosis and a heart attack or stroke. This dissertation considered the role of plaque microstructure in the mechanics and rupture risk of atherosclerotic plaques. Fibre structures in human atherosclerotic plaques were characterised through scanning electron microscopy, histology, and image processing. Local primary fibre orientation and the fibre dispersion were calculated. Plaque shoulder regions, where rupture is most frequent, had higher fibre dispersion and were more misaligned with the lumen wall. Comparative FE models were made from the plaque geometries and fibre structures found by image processing: one with evenly dispersed fibres (isotropic) and one with a preferred fibre orientation (anisotropic). The isotropic and anisotropic FE models predicted significantly different stresses. Stresses were often highest in the shoulder regions. Anisotropic stresses were calculated relative to fibres: axial stresses were highest, shear stresses were intermediate, and transverse stresses were low. Since the tissue is strongest in the fibre direction (axially), axial and shear failure modes should be considered. Material tests (uniaxial tension, trouser tear, and notched specimen) were used to characterise material properties in healthy porcine arteries. Fibre structures were evaluated by histology, multiphoton microscopy, and image processing. Samples were stiffer circumferentially and toughest against radial tears. Fractures progressed between fibres, rather than by breaking them. Material properties and fracture mechanisms were explained by fibre structures. In summary, atherosclerosis altered the fibre structure of the arteries, in ways that were mechanically significant and that explained clinical observations.
Supervisor: Sutcliffe, Michael ; Teng, Zhongzhao Sponsor: WD Armstrong Trust ; NSERC
Qualification Name: Thesis (Ph.D.) Qualification Level: Doctoral
Keywords: Cardiovascular ; Atherosclerosis ; Microstructure ; Fibre ; Rupture ; Stress ; Coronary ; Carotid ; Mechanics