Title: Production of anisotropic injection moulded NdFeB magnets from end-of-life sintered magnets
Author: Farr, Matthew
Awarding Body: University of Birmingham
Current Institution: University of Birmingham
Date of Award: 2018
Availability of Full Text:
Access from EThOS:
Full text unavailable from EThOS. Thesis embargoed until 31 Dec 2021
Access from Institution:
Abstract:
In this work, the hydrogenation-disproportionation-desorption-recombination (HDDR) processing conditions were optimised for scrap sintered NdFeB magnets from hard disk drives (HDDs). The HDDR process was then performed on scrap sintered NdFeB magnets, which were separated from HDD assemblies using hydrogen, on a large scale in order to produce anisotropic NdFeB alloy powder. The HDDR powder was then used to produce injection moulded magnets on pilot scale equipment (5 kg load) at Kolektor Magnet Technology GmbH, Germany. Sintered NdFeB magnets were separated from cropped hard disk drive corners as a hydrogenated powder, before being purified to remove any contaminants. The material was then HDDR processed using parameters optimised for this material (900 °C and 1200 mbar). The powder was compounded with polyamide 12 at a 90/10 ratio of HDDR powder to binder before injection moulding in a 500 mT field to form bonded magnets. The best bonded magnets produced had a remanence of 0.64 T, a coercivity of 623 kA/m and a BHmax of 61.7kJ/m\(^3\). Despite the mixed composition input feed, there was very little variation in the magnetic properties between 5 randomly selected magnets where a standard deviation for BHmax of 0.34 kJ/m\(^3\) was observed.
Supervisor: Not available Sponsor: Not available
Qualification Name: Thesis (Ph.D.) Qualification Level: Doctoral
EThOS ID: uk.bl.ethos.742626  DOI: Not available
Keywords: TN Mining engineering. Metallurgy
Share: