Title: Development and characterisation of a Portland cement-based dental root filling material
Author: O'Beirne, Joanne L.
ISNI:       0000 0004 2704 3799
Awarding Body: University of Birmingham
Current Institution: University of Birmingham
Date of Award: 2011
Availability of Full Text:
Access from EThOS:
Access from Institution:
Mineral trioxide aggregate (MTA) is a Portland cement (PC)-based endodontic material used for sealing root canals. This study investigated the effect of calcium sulphate additions for improving the undesirably-long setting time of MTA-like dental materials, whilst maintaining the mechanical, biological and sealing properties. 10wt%PoP accelerated initial setting times of grey and white model cements and MTA from >6h to <40min, and did not significantly change compressive strengths and relative porosities with long-term storage in media. Cement pastes containing PoP may „false‟ set or stiffen through gypsum precipitation, seen in scanning electron photomicrographs of MTA-like cements with 30wt%PoP. Similar in vitro responses of adult and neonatal BMSC, periosteal and osteoblastic cultures were noted with PoP-modified and unmodified cements. Inhibition of cell growth was seen with 3day-cultures containing modified model cements and MTA, the possible result of calcium hydroxide release from cements. Sealing properties were characterised using dye leakage studies and concluded that the sealing abilities of model cements and MTA were not compromised by PoP addition. In summary, 10wt%PoP has shown potential as a modification to MTA by reducing the setting time whilst maintaining mechanical stability, solubility, in vitro responses to and the sealing properties of MTA, therefore, warrants further investigation.
Supervisor: Not available Sponsor: Not available
Qualification Name: Thesis (Ph.D.) Qualification Level: Doctoral
EThOS ID:  DOI: Not available
Keywords: Q Science (General) ; T Technology (General) ; RK Dentistry ; R Medicine (General)