Use this URL to cite or link to this record in EThOS: https://ethos.bl.uk/OrderDetails.do?uin=uk.bl.ethos.449726
Title: The theory and significance of retained austenite in steels
Author: Bhadeshia, Harshad Kumar Dharamshi Hansraj
ISNI:       0000 0001 3463 0455
Awarding Body: University of Cambridge
Current Institution: University of Cambridge
Date of Award: 1980
Availability of Full Text:
Access from EThOS:
Full text unavailable from EThOS. Please try the link below.
Access from Institution:
Abstract:
The processes leading to the retention of small quantities of austenite following the bainite and martensite phase transformations have been examined, together with the influence of retained austenite on the properties of low alloy steels. It was found that the upper and lower bainite transformations are separate reactions, although both involve a displacive transformation mode, Growth seems to occur by the repeated nucleation of martensitic sub-units, and this leads to an apparently slow growth rate, The partitioning of carbon from bainitic ferrite into residual austenite was thermodynamically proven to occur subsequent to transformation, and was shown to be directly responsible for the 'incomplete reaction phenomenon'. The nature of sympathetic nucleation and of the limited size of bainitic sub-units was rationalised in terms of the relatively low driving force available for bainite transformations. It was shown that the retention, stability and morphology of austenite could be directly derived from the basic transformation mechanism. Under certain circumstances, the bainitic retained austenite conferred exceptional strength/toughness properties to silicon steels; these were· shown to be superior to the properties associated with tempered martensite microstructures, Using thermodynamics, a model was established which could predict the toughness behaviour of silicon steel bainites simply from a knowledge of the composition. The tempered martensite embrittlement phenomenon was not found to be directly linked to the decomposition of retained austenite films, but to the coarsening of inter- or intra-lath carbides. In dislocated martensites, it was found that the distribution and quantity of retained austenite could be rationalised in terms of the degree of accommodation between adjacent martensite variants. The incipient twins generally observed in lath martensites were shown to be accommodation defects such that the extent of twinning was the greatest when adjacent martensite units had twin-related lattices. The thermodynamics of dislocated martensites have been briefly examined, The inhomogeneous deformation behaviour of dual-phase steels has been analysed in terms of available models.
Supervisor: Edmonds, David Vernon Sponsor: Royal Armament Research and Development Establishment, Fort Halsted
Qualification Name: Thesis (Ph.D.) Qualification Level: Doctoral
EThOS ID: uk.bl.ethos.449726  DOI:
Keywords: steels ; bainite ; metallurgy ; physical metallurgy ; retained austenite ; phase transformation ; solid state ; cementite ; martensite ; crystallography ; dual phase steel ; tempered martensite ; thermodynamics ; diffusionless transformation ; epsilon carbide ; austenite ; silicon