Title: Hydrogen release and absorption in mixed anion lithium amide/lithium ternary nitride systems
Author: Nguyen, Trang Thi Thu
ISNI:       0000 0004 5914 8851
Awarding Body: University of Birmingham
Current Institution: University of Birmingham
Date of Award: 2016
Availability of Full Text:
Access from EThOS:
Access from Institution:
Abstract:
In this work, reactions of either LiBH\(_4\), ZnCl\(_2\) or Zn\(_3\)N\(_2\) with LiNH\(_2\) have been studied. The presence of CoO significantly affected the products and hydrogen release on heating mixtures of χLiBH\(_4\)-γLiNH\(_2\). The ratios of the l4\(_1\)/amd and the P2\(_1\)/c polymorphs of Li\(_3\)BN\(_2\) in the products have been changed under different conditions studied. On addition of CoO, the temperature of hydrogen release from the χLiBH\(_4\)-γLiNH\(_2\) systems was greatly reduced, starting from 100°C and peaking around 250°C, much lower than 240°C and 330°C without catalyst. Ball-milling helped to improve the amounts of hydrogen desorbed from 3–4 wt% up to ≥10 wt%. In the reactions of ZnCl\(_2\) + nLiNH\(_2\) (where \(\textit n\) = 2–6), main products were LiCl, Zn\(_3\)N\(_2\), and LiZnN. NH\(_3\) was the main gas released from these reactions and the addition of LiH changed NH\(_3\) into H\(_2\), which was released around 90°C, much lower than in the absence of LiH. A mixture of LiZnN and LiCl obtained from this reaction was partly rehydrogenated to form Li\(_2\)NH and Zn. The reaction of Zn\(_3\)N\(_2\) and LiNH\(_2\) was found to produce pure LiZnN without LiCl. Neither pure LiZnN nor Zn\(_3\)N\(_2\) could be hydrogenated under the conditions tried, but a mixture resulting from the reaction could react with H\(_2\) to form LiNH\(_2\) and Zn. The cyclability of the Li–Zn–N system showed an ability to release and take up gases under different pressure conditions. Mg-doping in LiZnN was examined to improve reversibility of the Li–Zn–N system but was not successful.
Supervisor: Not available Sponsor: Not available
Qualification Name: Thesis (Ph.D.) Qualification Level: Doctoral
EThOS ID: uk.bl.ethos.685391  DOI: Not available
Keywords: QD Chemistry
Share: