Use this URL to cite or link to this record in EThOS: http://ethos.bl.uk/OrderDetails.do?uin=uk.bl.ethos.552336
Title: The rechargeable lithium/air battery and the application of mesoporous Fe₂O₃ in conventional lithium battery
Author: Bao, Jianli
Awarding Body: University of St Andrews
Current Institution: University of St Andrews
Date of Award: 2009
Availability of Full Text:
Access through EThOS:
Full text unavailable from EThOS. Thesis embargoed until 24 Nov 2017
Access through Institution:
Abstract:
By replacing the intercalation electrode with a porous electrode and allowing lithium to react directly with O₂ from the air, the new rechargeable Li/O₂ battery system was studied. The porous cathode is comprised of carbon, catalyst and binder. The effect of every component was investigated. The catalyst was believed to play an important role in the performance of the electrode. A number of potential materials have been examined as the catalyst for the O₂ electrode. It suggests that the nature of the catalyst is a key factor controlling the performance of the O₂ electrode. Several catalysts based on first row transition metal oxides each with three different morphologies, bulk, nanoparticulate and mesoporous were studied. The influence of the morphology on the discharge and charge voltage, discharge capacity and cyclability were examined. Among all the catalysts studied, α-MnO₂ nanowires was found to be the best candidate. The reversible capacities of 3000 mAhg⁻¹(normalised by the mass of carbon) or 505 mAhg⁻¹ (based on the total mass of cathode + O₂ ) was obtained. Some of other factors, such as type of carbon, type of binder, type of electrolyte, the construction of cathode and the modification of the catalyst were also investigated, even just in the early stage. Capacity fading during cycling is the main problem in all the cases. A number of experiments were carried out to understand and attempt to avoid the fading problem. After successful synthesis of mesoporous α-Fe₂O₃ with unique properties (by Jiao et al.), the application of these materials in conventional Li battery was studied. Mesoporous α-Fe₂O₃ with ordered walls, mesoporous α-Fe₂O₃ with disordered walls and Fe₂O₃ nanoparticles were examined. It was also applied to examine the different factors that influence the rate of conversion electrodes, i.e., Li⁺ and e⁻ transport to and within the particles, as well as the rate of the two-phase reaction, demonstrating that for this conversion reaction electron transport to and within the particles is paramount.
Supervisor: Bruce, Peter Sponsor: Not available
Qualification Name: Thesis (Ph.D.) Qualification Level: Doctoral
EThOS ID: uk.bl.ethos.552336  DOI: Not available
Keywords: TK2941.B27 ; Storage batteries ; Lithium cells ; Cathodes--Materials ; Mesoporous materials