Title: Novel precursors for chalcogenide materials
Author: Oyetunde, Temidayo Timothy
Awarding Body: University of Manchester
Current Institution: University of Manchester
Date of Award: 2011
Availability of Full Text:
Access through EThOS:
Access through Institution:
Abstract:
Metal chalcogenides (sulfides, selenides and tellurides) are materials of current interest due to their peculiar properties such as optoelectronic, magnetooptic, thermoelectric and piezoelectric displays. These semiconducting materials have potential applications in solar cell devices, infrared detectors and ambient thermoelectric generators. Previously, these materials have been deposited by multiple-source precursor route with several problems associated with this technique. This work describes the synthesis of metal complexes (Zn, Cd, Fe, Ni, Pd, Pt) using the imidodichalcogenodiphosphinate ligand (Woollins ligand). Their thermal decomposition together with structural and spectroscopy analysis was carried out. The complexes were used as single source precursors for the deposition of cadmium selenide, cadmium phosphide, cadmium sulfide, zinc selenide, iron selenide and the tellurides of nickel, palladium, platinum and iron as thin films and powders. These were deposited by AACVD and pyrolysis. The deposited thin films and powders were characterised by powder X-ray diffraction (PXRD), scanning electron microscopy (SEM), energy dispersive analysis of X-rays (EDAX), X-ray photoelectron spectroscopy (XPS) and superconducting quantum interference device (SQUID). The cadmium complexes [Cd{iPr2P(Se)NP(Se)iPr2}2] and [Cd{iPr2P(S)NP(Se)iPr2}2] deposited the mixture of hexagonal CdSe and monoclinic Cd2P3 films at the flow rate of 160 sccm at 475 and 500 °C. At the flow rate of 240 sccm, only hexagonal CdSe was deposited from [Cd{iPr2P(Se)NP(Se)iPr2}2] at all temperatures. Hexagonal CdS and the mixture of orthorhombic Cd6P7/cubic Cd7P10 were deposited from [Cd{iPr2P(S)NP(S)iPr2}2]. The zinc complexes [Zn{iPr2P(Se)NP(Se)iPr2}2] and [Zn{iPr2P(S)NP(Se)iPr2}2] both deposited cubic ZnSe at all temperatures with the flow rates of 160 and 240 sccm. The iron complexes [Fe{(SePPh2)2N}2] and [Fe{(SePPh2NPPh2S)2N}2] deposited orthorhombic FeSe2 mixed with monoclinic Fe3Se4 by pyrolysis at 500 and 550 °C. An unresolved pattern was observed from the complex [Fe{(SePPh2NPPh2S)2N}2] at 550 °C. XPS analysis of the deposited FeSe2 showed the surface oxidation of the material, while the magnetic measurements on the sample using SQUID confirmed its ferromagnetic properties. The telluride complexes of nickel, palladium, platinum and iron deposited the metal telluride respectively as: hexagonal NiTe, hexagonal PdTe, hexagonal PtTe2 (mixed with rhombohedral PtTe) and hexagonal FeTe2. Conductivity studies on NiTe and PdTe revealed them to be insulators, while the magnetic measurements on FeTe2 indicated its antiferromagnetic behaviour.
Supervisor: O'Brien, Paul Sponsor: Not available
Qualification Name: Thesis (Ph.D.) Qualification Level: Doctoral
EThOS ID: uk.bl.ethos.549341  DOI: Not available
Keywords: Single-source Precursors, CVD, Chalcogens, selenides, sulfides, tellurides ; semiconductors, direct band-gap, TGA