Title: Investigating the effect of processing parameters in the electrospinning of nanofibres
Author: Chowdhury, Mohammad Mahfuzur Rahman
Awarding Body: Heriot-Watt University
Current Institution: Heriot-Watt University
Date of Award: 2010
Availability of Full Text:
Access from EThOS:
Access from Institution:
Abstract:
Nylon 6, Nylon 6.6, PEO/water, PEO/water/Ethanol, PVA/FeCl3 and PEO/wood pulp have been successfully electrospun into nanofibres in the range of 200 nm to 1500 nm. A comprehensive understanding of the effect of processing parameters on the morphological structure of these nanofibres has been established. Parameters such as concentration of polymer solution, applied voltage, electrospinning collection distance and flow rate have been found to affect fibre morphology. For Nylon 6 and Nylon 6.6 uniform nanofibres were produced using polymer solution concentrations, 20 wt.% and 25 wt.%, applied voltage of 15 kV, spinning distance of 8 cm and volume feed rate of 0.20 ml/hr. The produced nanofibres average diameter was 924 nm and 827 nm. For PEO/water, PEO/water/Ethanol and PEO/wood pulp optimum conditions of polymer solution concentration of 14 wt.% and 10 wt.%, an applied voltage of 15 kV, spinning collection distance of 11cm and volume feed rate of 0.20 ml/hr and 0.25 ml/hr, produced uniform nanofibres. The produced nanofibres average diameter was 452 nm, 544 nm and 494 nm. As for PVA/FeCl3, optimum conditions of polymer solution concentration of 8 wt.%, an applied voltage 15 kV, spinning collection distance 11 cm and flow rate 0.25 ml/hr produced uniform magnetic nanofibres. The produced nanofibres average diameters were 789 nm. These parameters have consequently been optimized to obtain uniform quality at different ranges of nanofibres. In this context it was established that the processing parameters vary significantly from one polymer to another but in general, the concentration the most important role in obtaining uniform fibre diameter without thin and thick places and beads. Applied voltage also played a significant role in determining the diameter of nanofibres and little significant effect on the fibre morphology was observed with the variation of spinning collection distance and noticeable structural change with a change in the solution flow rate. A selective range of microscopic techniques such as, Scanning Electron Microscopy, Atomic Force Microscopy and Transmission Electron Microscopy were used to characterise and evaluate the nanofibres produced during this study. DSC, X-ray diffraction and FTIR was used to identify the thermal properties of Nylon 6.6, PEO and PEO/wood pulp nanofibres produced. Nanofibres produced in this study have a wide range of potential applications in different fields, including, biomedical, magnetic sensor, mats for composite protective clothing, filtration, aerospace and others.
Supervisor: Not available Sponsor: Not available
Qualification Name: Thesis (Ph.D.) Qualification Level: Doctoral
EThOS ID: uk.bl.ethos.547698  DOI: Not available
Share: