Title: The beneficiation of steel making slags
Author: Gokemre, M. Levent
Awarding Body: University of Aston in Birmingham
Current Institution: Aston University
Date of Award: 1980
Availability of Full Text:
Access through EThOS:
Access through Institution:
Abstract:
The thesis examines the possibilities for the beneficiation of steel making slags by using mineral processing methods. Chemical and Mineralogical investigations have been carried out by SEM and EP}ffi to determine the most suitable separation methods in terms of crystal size, chemical composition and surface properties. Magnetic separation was applied in connection with size reductions for the extraction of the metallic iron prills and other iron containing phases and the results were related to the feed size and operating conditions. The behaviour of the slags in flotation tests was studied with respect to the recovery and grade. It was found that the free lime presence in the slags caused a high acid consumption of both weak and strong acids. It also reacted with acids and consequently produced a white precipitate, (CaS04 for H2 S04 ). The poor response of the phases to the flotation by different types of collector was found to be due to surface alteration caused by the free lime. The flocculation tests were carried out at the natural pH of the slags to prevent surface alterations. Settling tests were done to determine the suitable flocculants for the separation tests. The effect of the settling period, flocculant concentration, conditioning period and number of cleaning cycles were determined to optimize the separation tests. The discussion brings together this study with previous theoretically based work cited in the literature to elucidate the factor5governing the utilisation of steel making slags.
Supervisor: Not available Sponsor: Not available
Qualification Name: Thesis (Ph.D.) Qualification Level: Doctoral
EThOS ID: uk.bl.ethos.545192  DOI: Not available
Keywords: Engineering Materials ; Metallurgy
Share: