Title: Hot spots in ammonium nitrate
Author: Taylor, Nicholas
Awarding Body: University of Cambridge
Current Institution: University of Cambridge
Date of Award: 2011
Availability of Full Text:
Access through EThOS:
Full text unavailable from EThOS. Please try the link below.
Access through Institution:
Abstract:
Ammonium nitrate (AN) is commonly used as an explosive and as a fertilizer. In both roles it is provided as prills or pellets, approximately spherical and a few millimetres in diameter. The microstructures of several commercially-available AN compositions were investigated usingenvironmental scanning electron microscopy (ESEM) and X-ray microtomography. Those intended for explosive use were found to bemore porous than those intended for fertilizer use. The pores in explosiveprills were also found to form a connected network. The elemental composition of pellets of mixed AN and dolomite was investigated using energy-dispersive X-ray spectroscopy (EDX); the dolomite additivewas found to take the form of grains roughly 50 μm in size. The compaction behaviour of confined cylindrical beds of these prillsand pellets was studied at strain rates between 4 x 10-4 s-1 and 200 s-1. Quasi-static experiments were performed using a screw-driven instrumented press, while higher-rate experiments used a drop weight,instrumented with a line laser and load cell. The resistance of a bed to compaction was found to depend on the microstructure of its prills in most cases. Denser prills offered greater resistance to compaction. The exception to this rule was a pellet, rather than prill, formulation. Beds were also found to offer more resistance to compaction at higher strain rates. The Kawakita compaction model was found to agree well with the experimental data. A commercial fertilizer, not containing any AN, was assessed for use as an inert mock for AN prills and pellets. Prills of a suitable size for this purpose were found using EDX to consist of P2O5, with a coatingof unknown composition. They were supplied mixed with smaller K2CO3 and urea prills. The mixture was found to have comparablecompaction behaviour to AN compositions, indicating that it was useful as a mock for those compositions. In a plate impact experiment on a single layer of P2O5 prills, very little light was observed. Thisindicated that these prills were sufficiently inert for these purposes. The light produced by shocked granular ammonium nitrate beds and single prill layers was investigated using high-speed framing photography, photodiodes and gated visible-light spectroscopy. Framing photography of prill layers suggested that reaction in prill beds was dominatedby effects internal to prills. This was further supported by the similarity between photodiode recordings of prill beds and beds of inert prills containing a single reactive prills. Framing photography of drop weight experiments searching for a mechanism for initiation of reaction by interaction between prills found nothing. Decay of the light output of the beds suggested that in both granularand prill beds this light output was due to small regions heated to thousands of kelvin, which then cooled. Spectroscopic study confirmed this. These regions were found to reach a peak temperature of 6660 ± 20 K, well in excess of the approximately 2000 K predicted by a simple chemical model. Investigation of spectral lines observedduring this study indicated that the exothermic reaction that led to heating of these emitting regions involved NO.
Supervisor: Allison, William Sponsor: Not available
Qualification Name: Thesis (Ph.D.) Qualification Level: Doctoral
EThOS ID: uk.bl.ethos.541934  DOI: Not available
Keywords: s ; Ammonium nitrate ; Detonation ; Shock ; Granular material ; Compaction